fluoride alumini
auiliili oloa
faasino Igoa |
AF-0 |
AF-1 |
AF-2 |
AF-3 |
Fluorine (F)% min |
61 |
60 |
58 |
58 |
Sodium (NA) Max% |
0,30 |
0,40 |
2.8 |
2.8 |
Alumini (Al)% min |
31,5 |
31,0 |
29,0 |
29,0 |
Loi I le 550 ° Max% C |
0.5 |
1.0 |
5.5 |
5.5 |
Oxide Silicon (Sio 2) Max% |
0,10 |
0,30 |
0,30 |
0,35 |
Oxide Ferric (Fe 2Le 3) Max% |
0,06 |
0,10 |
0,12 |
0,12 |
Sulphate (Ina 4) Max% |
0,10 |
0,6 |
1.0 |
1.0 |
Pentoxide (P 2Le 5) Max% |
0,03 |
0,04 |
0,04 |
0,04 |
Density tele (g / cm 3) min |
1.5 |
1.3 |
0,7 |
0,7 |
O teisi soluble i le vai ma le tele soluble i HF suavaia. Le meatotino vailaau mo le fluoride alumini maualuga density e matua tumau, ae o loo i ai le a decomposed vai tioata faapitoa i Al 2Le 3 i le vevela maualuga i le tatalaina HF.
Faaaogaina: E le faaaogaina faapitoa o se Fetuutuunai sooupu mo electrolyte i alumini smelting e fused electrolysis masima, foi i keramika glaze, vaega taua ma flux o nonferrous isi metallurgy uamea
Teuina: I -O le palasitika lalagaina taga po o le ato lalaga i ata tifaga palasitika totonu, 40kgs, 50kgs, po 1000kgs upega taitasi, po o i le manaoga o tagata e faaaogāina auaunaga.